Refrigerator for Fresh Meat and Fruit Polyurethane Foam Refrigerator Refrigeration

• Customization: Available
• CAS No.: 9016-87-9
• Formula: 9016-87-9
• Model NO.: ZHD-8001
• EINECS: 9016-87-9
• Source: Pol/ISO
• Appearance: Liquid
• Grade Standard: Industrial Grade
• Colour: Light Yellow
• Hydroxyl Value Mgkoh/G: 350-450
• Density (20ºC) G/Ml: 1.1±0.02
• Viscosity: 3500-4500
• Specific Gravity: 1.05-1.10
• C-P Entane: Part by Weight 12-13
• Density(Kg/M3): >=35
• Closed Cell Rate (%): >=90
• Dimensional Stability(%): Low Temperature (-30ºC, 24HS) 1.0
• Dynamic Viscosity (25ºC) MPa.S: 3500-4500
• Storage Temperature ºC: 10-25
• Hydroxy Value: 350-450
• Blend Polyol: Part by Weight 100
• Isocynate: Part by Weight 134.4-135.6
• Thermal Conductivity (10ºC) W/M.K: ≤0.022
• Compressive Strength(10%),Kpa: 150
• Transport Package: Iron Drum/IBC/Tank
• Specification: 200-220KGS/Drum
• Trademark: Zibo Huide
• Origin: Zibo, China
• HS Code: 3907299090
• Production Capacity: 100, 000ton/Year

Product Description

Simple introduction (product features)
1)good flowability
2)foam density distribute uniformity                              
3)low thermal conductivity                                                                       
4)excellent low temperature dimensional stability
General description
ZHD-8001 is a semi resin premix combined polyol, based on polyether polyol, formulated with catalyst,blowing agent,stabilizing agents and other additves(if necessary) according to a parameter.It is a fully formulated polyether polyol developed for the rigid insulation of refrigerators and freezers. Blowing is provided with C-pentane.It is the mixture of polyol.

Technical Quality Conditions

Physical characteristics(without c-pentane)
                                                                                              
Item                            Unit                    Index
                                                                                              
Appearance                     light yellow transparent liquid
Viscosity           25ºC,mPa.S              3500-4500
Hydroxy Value       mgKOH/g                350-450
Specific gravity         25ºC                 1.05-1.10
                                                                                              

Physical characteristics(with c-pentane)
                                                                                               
Item                           Unit                    Index
                                                                                               
Appearance                     light yellow transparent liquid
Viscosity           25ºC,mPa.S              700-900
Specific gravity        25ºC                  1.05-1.10
                                                                                               

Process and reactive characteristics( actual value varied depends on the processing conditions)
Foaming condition
Manual mixing
Component temperature:20-25ºC
Mixing speed:5000rpm/8 sec

Machine
Mold temperature:35-40ºC
Component temperature: 20-25ºC

Recommended ratio

Component	Part by weight	Remark
Blend polyol	100
C-pentane	12-13
Isocynate	134.4-135.6	P/M=100/120

Foam characteristics

ITEM		PROPERTY
Density(kg/m3)	Core	>=35
Thermal Conductivity (10ºC) W/m.k		≤0.022
Closed cell rate (%)		>=90
Compressive strength(10%),kpa		150
Dimensional stability(%)	Low temperature (-30ºC,24hs)	1.0
	High temperature (70ºC,relative humidity95%±5%,24hs)	1.5

Above Data is for reference only.Actual values vary depending on processing conditions and species.

Main Applications
rigid PU foam cores for insulation of refrigerators and freezers in combination with isocyanate (MDI).
                       
Preparation
Before using,this polyol has to be mixed very well..

STORAGE OF MATERIALS

The  materials  are  sensitive  to  humidity  and  partially  used  drums  should  be  tightly  sealed  to prevent the ingress of moisture.

 

ZHD-8001-A (Polyol Blend)
The Polyol blend has a shelf life of three months from date of manufacture when stored indoors at temperatures of 20-30°C. The Polyol blend should be thoroughly mixed before use.

ZHD-8001-B (Isocyanate)
The Isocyanate has a shelf life of one year from date of manufacture when stored indoors at temperatures of 20-30°C. Avoid storage temperatures of below 0°C  (as  some  crystallization may occur) or above 50°C (as formation of insoluble so lids may occur).

 

SAFTY PRECAUTIONS
Direct contact with ZHD-8001 can lead to moderate eye irritation and mild skin irritation, which can cause skin allergies. Repeated inhalation of high concentration of volatile gas will cause respiratory allergy, and should be treated immediately. Anti- inflammatory and anti-allergic treatment measures should be taken. Please be careful in the operation to prevent contact with the skin and splash into the eye, please wear the necessary protective equipment (gloves, protective goggles, working clothes, etc.). Once splashed on the skin or the eye, rinse with water immediately for at least 15 minutes, and the skin is washed with soapy water. Please seek medical treatment immediately after swallowed.

Notice: This product specification is intended to be used by Shunda Polyurethane Company in order to show sincerity to our customers, while it is not covered by law as a guarantee. Customers can adjust according to the actual operating conditions. If you have any questions, please call our company and we will serve you wholeheartedly.

FAQ
1.F:Why choose your company?
  Q:Huide Company founded in year 2010,is a leading manufacturer of rigid PU foam blend polyol system materil, we have professional team,our products are stable andservice is decent.
2.F:Could you send me samples?
  Q:Yes,sure. Normally,we can supply free sample for less than 5kg.But need the customer take charge of the express cost.
3.F:Are you a trader or manufacturer?
  Q:We are manufacturer.We do our own blend polyol for over 15 years in china.
4.F:What's the MOQ?
  Q:1 Drum.
5.F:What's the lead time?
  Q:Within 3-5 days after payment.